Abstract
Vacancy ordered maghemite (γ-Fe2O3) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca10(PO4) 6(OH)2) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C6H8O7) onto γ-Fe2O3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy. From XPS surface analysis, two binding energies related to oxygen were attributed to bindings between C6H8O7/γ- Fe2O3 and C6H8O7/HAp from an interfacial reaction promoted by strongly adsorbed H2O molecules at the surface of these nanomaterials. Le Bail refinement of the XRD patterns showed the formation of well-crystallized pure tetragonal maghemite before and after functionalization with nanoHAp. The temperature dependence of hyperfine parameters of pure and functionalized γ-Fe2O3 nanoparticles was investigated via Mössbauer spectroscopy. TEM revealed the formation of quasi-spherical γ- Fe2O3 nanoparticles with an average diameter of ca. 12nm and 16nm before and after functionalization with nanoHAp in agreement with Le Bail refinement. Magnetometry measurements showed a saturation magnetization of 12emu/g and a blocking temperature of 340K for the functionalized γ- Fe2O3 nanoparticles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.