Abstract
Ultraviolet and visible absorption spectra of prepared undoped lithium phosphate glass and samples of the same nominal composition with additional Bi2O3 contents were measured before and after being subjected to gamma doses of 3 and 6 Mrad. The base undoped lithium phosphate glass exhibits strong charge transfer ultraviolet absorption bands, which are related to unavoidable presence of trace iron impurities within the raw materials for the preparation of this glass. Bi2O3-containing glasses show the extension of UV absorption beside the resolution of visible bands at 400, 450, and 700 nm with the increase of Bi2O3 content due the sharing of absorption of Bi3+ ions. Gamma irradiation of the base glass reveals extended induced bands; the UV bands are related to the conversion of some Fe2+ to Fe3+ through photochemical reactions during the irradiation process. The visible induced bands are related to the formation of positive hole centers from the host phosphate glass. Glasses containing Bi2O3 are observed to show some shielding behavior, which is attributed to the presence of heavy weight and large atomic number of Bi3+ ions. Infrared absorption spectral measurements of the base lithium phosphate glass show characteristic vibrational modes which are related to specific phosphate groups. The addition of Bi2O3 in measurable percent produces additional vibrational bands due to the introduction of Bi–O groups such as BiO3 and BiO6.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.