Abstract
The waterborne polyurethane-acrylate (PUA) oligomer was firstly prepared based on isophorone diisocyanate (IPDI), polyether polyol (NJ-210), dimethylol propionic acid (DMPA) and hydroxyethyl methyl acrylate (HEMA) via in situ and anionic self-emulsifying method. The UV-curable polyurethane-acrylate (UV-PUA) was obtained with oligomer, monomers (BA and TPGDA) and photoinitiator Darocur 1173. FT-IR, DSC and TGA were employed to investigate the structures and thermal properties of the UV-PUA films. The effects of BA/TPGDA ( R) value, the content of Darocur 1173 and the UV curing time on the performances were investigated. Some mechanical performances, solvent resistance and the gel content of UV-PUA films were measured. When the ratio of BA/TPGDA was 5/5, the UV-PUA film had the best solvent (water, alkali and ethanol) resistances. Besides, with the ratio of the BA/TPGDA increasing, the surface drying time increased. When the content of Darocur 1173 was 4%, the gel content achieved the maximum while the surface drying time achieved the minimum. The obtained UV-curable polyurethane-acrylates are promising as oligomers for UV-curable coatings, plastics, inks and adhesives.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.