Abstract
AbstractPitch subdivision of tantalum nitride (TaN) lines is demonstrated across a 200 mm wafer using a cyclic quasi‐atomic layer etch process in an inductively coupled plasma reactor. Chlorine (Cl2) and hydrogen (H 2) chemistries are introduced sequentially to an argon plasma in discrete steps to etch the TaN film. The starting lithographic pattern with critical dimension (CD) of approximately 82 nm and pitch of 200 nm thus yields lines of approximately 40 nm CD and 100 nm pitch with minimal line edge roughness increase. We identify a synergistic effect between H 2‐exposed TaN and Cl 2 plasma as contributing to this result, as well as a potential link to surface oxidation. Optical emission spectroscopy analysis of the plasma discharge is used to characterize reactive species densities and explain the observed changes in profile.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.