Abstract
A modified SAE 4118H steel was subjected to isothermal treatments between 700 °C and 400 oC every 50 °C range, with the intention of evaluating the decomposition of austenite at constant temperature. It was varied time of stay in the isothermal treatment between 15 and 28800 seconds depending on the treatment temperature. After each isothermal treatment and standard metallographic preparation, the samples were etched with color metallography reagents for revealing the microstructure obtained. At temperatures of 700oC to 550°C the steel showed microstructure composed of ferrite and pearlite. Between 500oC and 400°C bainitic microstructure was quickly formed. The reduction of treatment temperature provided finer microstructures, which increased the hardness of steel. With the use of color metallography reagents, excellent contrast for determining the volume fraction of microstructural constituents formed isothermally was obtained, helping the study of isothermal decomposition of austenite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.