Abstract
This work aims at studying the abrasion resistance of differently formulated organic–inorganic hybrid coatings prepared by sol–gel method. The organic phase contained UV curable urethane acrylate oligomers and monomers having different functionalities. The inorganic phase was composed of tetraethyl orthosilicate (TEOS) and 3-methacryloxy propyltrimethoxy silane (MEMO). Through a Taguchi experimental design, the impact of influencing parameters such as molar ratio of precursors, hydrolysis ratio (R), post-curing temperature, post-curing time and weight percentage of inorganic to organic part were investigated. Very high transparency of hybrid coatings indicated that nano sized inorganic phase had formed. MEMO could facilitate the connection of two phases, preventing macro phase separation. However, high levels of MEMO lead to ‘defect structure’ in silica network as well as to decreased transparency and mechanical properties. The optimum condition in which highly transparent films with great abrasion resistance occurred was observed at equimolar ratio of water to alkoxide and TEOS: MEMO ratio being unity. Statistical analysis revealed that thermal post-curing was not significantly important.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.