Usefulness of alkoxyltitanosiloxane for the preparation of mesoporous silica containing a large amount of isolated titanium

Abstract

Mesoporous silica containing a large amount of isolated Ti was prepared from an alkoxytitanosiloxane precursor through a hard template method. Isopropoxytris(tris-tert-butoxysiloxy)titanium ((iPrO)Ti[OSi(OtBu)3]3, TS3) was synthesized and TS3 was mixed with mesoporous carbon (CMK-3), a hard template. The mixture was pyrolyzed at 180°C to form a composite consisting of titanosilica and the hard template. After calcination at 600°C for the removal of the carbon template, the titanium species were not transformed to anatase TiO2, proved by DR-UV–Vis, FTIR, XPS, and XRD, while the ESR results indicated the presence of isolated Ti. The mesoporous structure was verified by SEM, TEM, and N2 adsorption. The Si/Ti ratio of the product was consistent with that of the precursor. All the results show that the material prepared from the precursor is ordered mesoporous silica containing a large amount of isolated Ti in the frameworks. The use of well-defined alkoxytitanosiloxane precursor leads to the formation of mesoporous silica with exactly controlled composition of titanium with neither loss of Ti nor transformation to anatase.