Abstract
This preliminary study introduces the incorporation and chemical stabilization of sulfur waste into a geopolymer matrix and explores the concept of material production for further environmental and engineering solutions. In this study, a novel synthesis procedure for sulfur-based geopolymers was introduced, and the role of sulfur in geopolymers and its optimal content to obtain a stable structure were explored. Geopolymers were synthesized by dissolving sulfur in an alkaline activator in different proportions. The alkaline solution was then mixed with metakaolin to synthesize the geopolymer matrix. Adding sulfur in amounts from 0 wt.% to 5 wt.%, compared with metakaolin, led to an increase in the compressive strength of the geopolymers from 22.5 MPa to 29.9 MPa. When sulfur was between 5 wt.% and 15 wt.%, a decrease in the compressive strength was observed to 15.7 MPa, which can be explained by defects and voids in the geopolymer’s microstructure due to the solubility of excess sulfur. Because of the incorporation of sulfur into the geopolymers, a compact and dense microstructure was formed, as reported in the SEM analysis. An XRD analysis showed that, besides quartz and analcime, a new phase, Al2·H10·O17·S3, was also formed as a result of sulfur dissolution in the alkaline activator of the geopolymers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.