Abstract
AbstractProgress in fabricating Cu(In,Ga)(S,Se)2 (CIGSSe) solar cells with Zn(S,O) buffer layers prepared by chemical bath deposition (CBD) is discussed. The effect of different Zn salt precursors on solar cell device performance is investigated using production scale CIGSSe absorbers provided by AVANCIS GmbH & Co. KG. The CBD process has been developed at the Hahn‐Meitner‐Institut (HMI) using zinc nitrate, zinc sulphate or zinc chloride as zinc precursor. An average efficiency of 14.2 ± 0.8% is obtained by using one‐layer CBD Zn(S,O) The dominant recombination path for well performing solar cells is discussed based on the results obtained from temperature dependent J (V) analysis. The structure and morphology of buffer layers deposited using zinc nitrate and zinc sulphate has been studied by means of transmission electron micrographs of glass/Mo/CIGSSe/Zn(S,O) structures. Results show a conformal coverage of the absorber by a Zn(S,O) layer of 15–25 nm consisting of nanocrystals with radii of ∼5 nm. XAES analysis of the buffer layer reveals a similar surface composition for buffer layers deposited with zinc nitrate and zinc sulphate. (© 2008 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.