Abstract
A new approach for the synthesis of Y3Al2Ga3O12 (YAGG) nanophosphors allowing the preparation of crystallites with sizes starting from 45 nm is presented. The controllability of the energy and trap density of the resulting material samples by annealing temperature was confirmed by thermoluminescence (TL) measurements. It has been shown that the annealing of samples at temperatures up to 1300 °C does not cause any substantial growth of crystallites, still remaining below 100 nm, but leads to changes in the activation energy of the persistent luminescence (PersL) process. On the other hand, annealing above 1400 °C results in grain growth on the submicron scale, which was confirmed by X-ray powder diffraction (XRPD) and electron transmission microscopy (TEM) measurements. In addition, with an increase in the molar ratio of urea to the total amount of metals used (R), qualitative changes are observed in the PersL process occurring from the excited states of Cr3+ and Pr3+ ions. This proves the influence of the synthesis process, in particular of the metal complexation at its initial stage, on the final structure ordering in the annealed materials. These observations are linked to previously reported defects in the YAGG structure, leading to PersL.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.