Abstract
Er3+ stabilized transparent α-Sialon ceramics with upconversion (UC) luminescence properties were fabricated for the first time by hot press sintering method. The fabricated samples show better transparency as well as UC luminescence properties. Moreover, the effect of Yb2O3 as a sensitizer on UC properties was analyzed in Er-α-Sialon system. The change in Sialon phases and crystal structure were analyzed by X-ray diffraction. The chemical compositions and morphology of grains and intergranular phase were analyzed by EDS and Transmission Electron Microscopy, respectively. The UC emissions were observed around 527, 547 and 670nm corresponding to the 2H11/2, 4S3/2 and 4F9/2 transitions, respectively when excited by 980nm continuous wave (CW) laser diode. UC process in Er3+ is found to be two photon processes. Intense green UC luminescence was observed with Er3+ and low amount of Yb3+ addition but higher amount of Yb3+ addition shows higher UC luminescence in red region. The transparency was higher in higher Er2O3 and low Yb2O3 content Sialon that was around 60% in visible light region. The chromaticity was also calculated for different samples and high color purity above 90% was obtained for green and yellow emissions. The mechanical properties were also investigated in this study.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.