Abstract
Er3+ doped Yb2Ti207 nanophosphors by Gd3+ codoping with nominal composition of (Er0.05Yb0.95-xGd3+)2Ti2O7 (x = 0, 0.2, 0.4, 0.6, 0.8, and 0.95) have been prepared by sol-gel method. Er3+-Gd3+ codoped Yb2Ti2O7 was characteristic of a typical face-centered cubic crystal phase, and the unit cell parameter increased linearly with the increase of Gd3+ concentration. Under a 976 nm laser diode excitation, both green and red upconversion emissions were observed and the upconversion emissions were enhanced significantly by Gd3+ codoping, showing the strongest green and red emissions at 80 mol% Gd3+ codoping. The intensity ratio of green to red emissions (Igreen/Ired) increased monotonously with the increase of Gd3+ concentration. The energy transfer between Yb3+ and Er3+ and the variation of local crystal field symmetry of Er3+ by the substitution of Yb3+ by Gd3+ ions led to the improvement of upconversion properties of Er3+-Gd3+ codoped Yb2TiO7 nanophosphors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.