Upconversion Luminescence and Color Tunability Properties in Tm3+-Ho3+-Yb3+ Co-Doped Oxyfluoride Nano-Glass-Ceramics

Abstract

Transparent oxyfluoride nano-glass-ceramics with highly efficient up-conversion and adjustable color luminescence were developed in the 50SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> -15AlF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -10BaF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> -15PbF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> -(9.3-x)GdF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -0.5YbF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -0.2TmF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -xHoF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> (x = 0.02, 0.05, 0.10, 0.50)composition in mol%. X-ray diffraction measurements revealed that heat treatments of the oxyfluoride glasses cause the precipitation of rare-earth ions co-doped fluorite-type of β-PbF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> in the glass matrix. Under 980 nm laser excitation, intense red, green and blue up-conversion luminescences were simultaneously observed in these transparent nanoglass-ceramics owing to the successive energy transfer from Yb <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3+</sup> to Ho <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3+</sup> and Tm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3+</sup> ions. Various colors of luminescence, including bright perfect white light, can be tuned by adjusting the concentrations of the Ho <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3+</sup> ions in the material. A possible energy transfer process and up-conversion luminescence mechanism in the nano-glass-ceramics are proposed and discussed.