Abstract
The RE3Al5O12 (REAG:Er3Al5O12, Er:Y3Al5O12 and Er:Yb3Al5O12) up-conversion (UC) nanocrystals have been prepared by the non-aqueous sol-gel method. The green and red UC emissions are attributed to the 2H(11/2), 4S(3/2) --> 4I(15/2) and 4F(9/2) --> 4I(15/2) transitions of Er3+, respectively, were obtained for all samples with a 975 nm semiconductor LD excitation. For Er3Al5O12 nanocrystals, the green and red UC emissions have similar intensities. Y and Yb ions have no evident effect on the peak positions, but strongly affected the intensities of the green and red UC emissions of the Er. A much higher intensity of the green relative to red UC emission was observed for Er:Y3Al5O12 nanocrystals, however, the red UC emission became predominant for Er:Yb3Al5O12 nanocrystals. It was suggested that the two-photon process was responsible for the green and red UC emissions mechanism for all the samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.