Abstract
In this paper, Y0.95 Er0.05 PO4 phosphor nanomaterial with tetragonal structure was successfully synthesized to realize NIR to VIS up-conversion. Synthesis control over the property of material was made in conventional hydrothermal method and controlled pressure method with nitrogen. X-Ray diffraction pattern confirmed the tetragonal phase of the crystals and further, morphology was studied using SEM. Under NIR excitation of 967nm, characteristic intermediate energy levels corresponding to Er3+ ion were observed. Blue, green and red emission was observed for the samples at room temperature which shows the possible use of this material for the fabrication of LED's.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.