Abstract
In this study, guinea starch nanoparticles (GSNP) were prepared by nanoprecipitation technique and modified with octenyl succinic anhydride (3 %) and pulsed electric field (1.5, 3.0, and 4.5 kV/cm). The effect of dual modification on the physicochemical, structural, morphological, thermo-pasting, and rheological properties of GSNP was investigated. The dual modification successfully incorporated octenyl groups into GSNP, as confirmed by 1H nuclear magnetic resonance spectroscopy and Fourier transform infrared spectroscopy. The degree of substitution increased from 0.0254 to 0.0347, with particle size ranging from 241.30 to 292.50 nm and zeta potential of −23.11 to −29.98 mV. TEM micrographs revealed that all SNP samples had self-aggregated granules with a mean size below 120 nm, and XRD confirmed a V-type crystalline structure. The amylose content and water absorption capacity decreased from 34.02 % to 24.63 % and from 2.45 to 1.91 g/g, respectively, while the oil absorption capacity and relative crystallinity increased from 3.42 to 4.01 g/g and from 17.82 % to 34.76 %, with modification. The gelatinization and degradation temperature of modified samples were higher while pasting properties exhibited variation with modification. The rheological properties of modified SNP samples exhibited more pronounced shear thinning, attributed to their weaker gel structure and fluid-like gel network. Overall, results suggested that modified GSNPs have potential for stabilizing Pickering emulsion and delivery of carrier materials for active functional substances.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.