Unveiling the Surface Chemical Reactions during Multi-Phase Catalytic Oxidation of Soot on Nanoengineering/Interfacing/Doping-Prepared Mn-CeO2 Catalysts Using TG-MS and Operando DRIFTS-MS.

Abstract

The aerosol pyrolysis method from nitrate precursors was used to prepare the Mn-CeO2 catalyst containing Mn2O3, CeO2, and Mn-doped CeO2 nanoparticles for catalyzing carbonous soot oxidation. The prepared Mn-CeO2 catalysts have high specific surface areas, Ce3+ ratio, and oxygen vacancy defects; these are a benefit for soot oxidation. The T50 for soot oxidation on the 0.57Mn-CeO2 catalyst is as low as 355 °C, which is 329 °C lower than that for soot oxidation without a catalyst. The catalysts were characterized using XRD, SEM-EDS, HRTEM, XPS, Raman spectroscopy, H2-TPR-MS, O2-TPD-MS, soot-TPR-MS, and operando DRIFTS-MS. The functions of Mn2O3, CeO2, and Mn-doped CeO2 in the 0.57Mn-CeO2 catalyst are unveiled. Mn-doped CeO2 plays a key role and CeO2 participates in soot oxidation, while Mn2O3 is used to enhance higher ratios of Ce3+, via the reaction of Mn3+ + Ce4+ = Mn4+ + Ce3+. The mechanism of soot oxidation on Mn-CeO2 was proposed.