Abstract
Massive carbon dioxide (CO2) emission from recent human industrialization has affected the global ecosystem and raised great concern for environmental sustainability. The solid oxide electrolysis cell (SOEC) is a promising energy conversion device capable of efficiently converting CO2 into valuable chemicals using renewable energy sources. However, Sr-containing cathode materials face the challenge of Sr carbonation during CO2 electrolysis, which greatly affects the energy conversion efficiency and long-term stability. Thus, A-site Ca-doped La1-xCaxCo0.2Fe0.8O3-δ (0.2 ≤ x ≤ 0.6) oxides are developed for direct CO2 conversion to carbon monoxide (CO) in an intermediate-temperature SOEC (IT-SOEC). With a polarization resistance as low as 0.18 Ω cm2 in pure CO2 atmosphere, a remarkable current density of 2.24 A cm-2 was achieved at 1.5 V with La0.6Ca0.4Co0.2Fe0.8O3-δ (LCCF64) as the cathode in La0.8Sr0.2Ga0.83Mg0.17O3-δ (LSGM) electrolyte (300 μm) supported electrolysis cells using La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) as the air electrode at 800 °C. Furthermore, symmetrical cells with LCCF64 as the electrodes also show promising electrolysis performance of 1.78 A cm-2 at 1.5 V at 800 °C. In addition, stable cell performance has been achieved on direct CO2 electrolysis at an applied constant current of 0.5 A cm-2 at 800 °C. The easily removable carbonate intermediate produced during direct CO2 electrolysis makes LCCF64 a promising regenerable cathode. The outstanding electrocatalytic performance of the LCCF64 cathode is ascribed to the highly active and stable metal/perovskite interfaces that resulted from the in situ exsolved Co/CoFe nanoparticles and the additional oxygen vacancies originated from the Ca2Fe2O5 phase synergistically providing active sites for CO2 adsorption and electrolysis. This study offers a novel approach to design catalysts with high performance for direct CO2 electrolysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.