Abstract
AbstractThe uniplanar orientation of poly(p‐phenylene terephthalamide) (PPTA) crystal was investigated by x‐ray and infrared measurements. Thin PPTA films 3–15 μm thick were prepared by coagulating a sulfuric acid solution of PPTA with various coagulants. Two types of uniplanar orientation were observed, depending on the coagulant used. Thin film coagulated with water exhibits (0k0) uniplanar orientation and film coagulated with other coagulants such as methanol, ethanol, and acetone exhibits (h00) uniplanar orientation. These (h00) and (0k0) uniplanar orientations are formed with crystal modifications I and II, respectively. The (0k0) uniplanar orientation transforms to (h00) upon annealing, accompanying crystal transformation from modification II to modifications I. These uniplanar orientations may result from anisotropic crystal growth due to polymer–coagulant interaction along the hydrogen bond direction. The effect of these uniplanar orientations on the mechanical properties was also examined. The thin film having the (0k0) uniplanar orientation shows ductile fracture, whereas the one having the (h00) uniplanar orientation shows brittle fracture upon tensile deformation. These results are explained on the basis of the direction of the uniplanar orientation of the hydrogen‐bonded sheet.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.