Abstract
Metal-organic framework (MOF) materials have been extensively incorporated with inorganic semiconductor photocatalysts to improve their photocatalytic activity through an efficient charge transfer process across their heterointerface. In this work, octahedral UiO-66-NH2 MOFs with edge-lengths of 110-330 nm are uniformly decorated on the surface of TiO2 electrospun nanofibers by a traditional solvothermal method combined with activation pretreatment. Before the solvothermal growth of UiO-66-NH2, the TiO2 electrospun nanofibers were activated in NaOH solution to etch the TiO2 surface for allowing the exposure of lattice oxygen. The exposed lattice oxygen on the TiO2 surface could interact with the MOF precursor of Zr4+ ions, thus enabling octahedral UiO-66-NH2 to grow uniformly on the surface of TiO2 nanofibers with an intimate Ti-O-Zr hetero-interface. Such an intimate hetero-interface provides an effective channel for boosting the electron transfer between UiO-66-NH2 and TiO2 in their heterostructure. Thus, the UiO-66-NH2/TiO2(anatase) heterostructures exhibited enhanced photocatalytic activity for H2 production as compared to either TiO2(anatase) nanofibers or UiO-66-NH2 nanooctahedra in the presence of Rhodamine B (RhB) as a sensitizer under visible light irradiation. In particular, the decoration of UiO-66-NH2 nanooctahedra on anatase/rutile mixed TiO2 nanofibers could induce further enhancement of the photocatalytic H2 production. The enhanced photocatalytic activity is attributed to the multi-step continuous interfacial transfer of photoinduced electrons with the way of RhB → UiO-66-NH2 → TiO2(anatase) → TiO2(rutile).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.