Abstract
Dense CaBi4Ti4O15 (CBT) ceramics with a unique texture were prepared by the reactive templated grain growth (RTGG) method using an extrusion technique. Plate-like Bi4Ti3O12 (BIT) particles, a reactive template for CBT, were mixed with other oxide and carbonate powders and unidirectionally aligned by extrusion. During sintering, oriented CBT grains were formed in situ topotaxially on the oriented BIT particles, and the templated grain growth and their densification eventually fabricated textured CBT ceramics. X-ray diffraction measurements and scanning electron microscopic observations revealed that the plate-like CBT grains were unidirectionally oriented parallel to the extruding direction without uniaxial alignment. Textured CBT ceramics poled in the extruding direction exhibited electromechanical coupling coefficients (k33) and piezoelectric coefficients (d33 and g33) more than two times as large as one of nontextured ceramics with the same composition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.