Uniaxial creep property and viscoelastic–plastic modelling of ethylene tetrafluoroethylene (ETFE) foil

Abstract

Ethylene tetrafluoroethylene (ETFE) foil has been widely used in spatial structures for its light weight and high transparency. This paper studies short- and long-term creep properties of ETFE foil. Two series of short-term creep and recovery tests were performed, in which residual strain was observed. A long-term creep test of ETFE foil was also conducted and lasted about 400 days. A viscoelastic–plastic model was then established to describe short-term creep and recovery behaviour of ETFE foil. This model contains a traditional generalised Kelvin part and an added steady-flow component to represent viscoelastic and viscoplastic behaviour, respectively. The model can fit tests’ data well at three stresses and six temperatures. Additionally, time–temperature superposition was adopted to simulate long-term creep behaviour of ETFE foil. Horizontal shifting factors were determined by W.L.F. equation in which transition temperature was simulated by shifting factors. Using this equation, long-term creep behaviours at three temperatures were predicted. The results of the long-term creep test showed that a short-term creep test at identical temperatures was insufficient to predict additional creep behaviour, and the long-term creep test verified horizontal shifting factors which were derived from the time–temperature superposition.