Abstract
It is important to understand glass alteration mechanisms and to determine their associated kinetics in order to develop models able to predict the alteration of nuclear, basaltic or archaeological glasses. Recent studies revealed that the respective contributions of diffusion, dissolution, condensation and precipitation processes in alteration are still a matter for debate. In this work, the alteration of a medieval-type glass (Si–K–Ca) was investigated as it presents a specific composition (without B and with low Al). Experiments were performed using a dynamic device, at 30°C, at pH 8 and 9 and during 1month in order to simulate alteration in contact with water (rainfall or condensation). The solution was doped in 29Si to discriminate between the silicon from glass (mainly 28Si) and from solution. The results showed that the external region of the alteration layer is devoid of modifier cations (K, Ca) and presents a 29Si/28Si ratio close to the solution one. This excludes that the alteration layer is a glass skeleton and highlights a progressive hydrolysis/condensation process, even if non-hydrolyzed silica tetrahedra could remain when the Si isotopic equilibrium is not reached. The internal zone appears to be gradually depleted in modifier cations and partly enriched in 29Si, but the thickness of this zone is overestimated using SEM-EDS and SIMS techniques. Even if in these experiments the dissolution mechanism is favored, the contribution of interdiffusion cannot be neglected to explain the weathering of ancient stained glassed windows in the atmosphere. The respective contribution of diffusion and dissolution are also discussed as a function of glass composition and surface texture, as well as of experimental conditions (alkaline pH, renewal of the solution).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.