Understanding the influence of tellurium oxide in front Ag paste for contacting silicon solar cells with homogeneous high sheet resistance emitter

Abstract

This paper investigates TeO2, one of the front Ag paste additives, to understand its role in low contact and gridline resistances for screen-printed Si solar cell. It is concluded that TeO2 aids the reduction of molten glass frit viscosity during contact co-firing. This in turn, leads to uniform flow of molten glass frit, both in the gridline bulk and interface of gridline and SiNx. Therefore, the uniform wetting and etching of SiNx and consequently larger contact area of metal to Si compared to its counterpart without TeO2. Hence, the current transport mechanism from Si to gridline can be said to be both direct and tunneling. The Raman spectra showed a blue shift in the phase of the TeO2 after contact co-firing in the gridline bulk confirming a crystalline γ-TeO2.