Ultrastructural Analysis of Er:YAG Lased Bovine Dentin Contaminated by Cariogenic Bacteria.

Abstract

Objective: The purpose of this study is to investigate the crystal structure of bacteria-contaminated bovine dentin after Er:YAG laser irradiation at various energy densities from macroscale, microscale, and nanoscale. Background: Er:YAG laser can change the morphology and chemical components of dentin. Few preliminary researchers investigate the laser effect on crystal in dentin tissue. Methods: Twenty dentin specimens from bovine incisors were cocultured with S. mutans (UA 159) and divided into four groups with diverse Er:YAG laser irradiation energy (0, 6.37, 12.73, 19.11 J/cm2). The ultrastructure of dentin before and after laser irradiation was investigated with nanoanalytical electron microscopy. X-ray diffraction provided the information of lattice parameters in dentin. The morphology of dentin was observed by scanning electron microscopy. High-resolution transmission electron microscope images and selected-area electron diffraction patterns were obtained for characterizing crystal domain size, structure, and microenvironment of dentin. Results: The combination of these methods disclosed that there exist mineralized, demineralized, and remineralized dentin in the bacteria-invaded dentin and can be feasibly recognized using morphological features. Laser treatments influence hydroxyapatite (HAp) crystals in dentin tissue in different ways: needle HAp in mineralized dentin tissue keeps intact with laser irradiation of no higher than 19.11 J/cm2; laser irradiation improves the crystallinity of lamella HAp by domain growth and rearranges its growth orientations. Conclusions: We report an unprecedented presence of remineralization zone consisting of lamella HAp crystals with distinct high-index planes. These findings have broad implications on the role of laser operation in driving biomineralization and shed new insights into a possible relationship between laser irradiation and remineralization.