Abstract
The present study reports synthesis and characterization of poly(MMA–co–BA)/ZnO nanocomposites using ultrasound-assisted in-situ emulsion polymerization. Methyl methacrylate (MMA) was copolymerized with butyl acrylate (BA), for enhanced ductility of copolymer matrix, in presence of nanoscale ZnO particles. Ultrasound generated strong micro-turbulence in reaction mixture, which resulted in higher encapsulation and uniform dispersion of ZnO (in native form – without surface modification) in polymer matrix, as compared to mechanical stirring. The nanocomposites were characterized for physical properties and structural morphology using standard techniques such as XRD, FTIR, particle size analysis, UV–Visible spectroscopy, electrical conductivity, TGA, DSC, FE-SEM and TEM. Copolymerization of MMA and BA (in presence of ZnO) followed second order kinetics. Thermal stability (T10%=324.9°C) and glass transition temperature (Tg=67.8°C) of poly(MMA-co-BA)/ZnO nanocomposites showed significant enhancement (35.1°C for 1wt% ZnO and 15.7°C for 4wt% ZnO, respectively), as compared to pristine poly(MMA–co–BA). poly(MMA–co–BA)/ZnO (5wt%) nanocomposites possessed the highest electrical conductivity of 0.192μS/cm and peak UV absorptivity of 0.55 at 372nm. Solution rheological study of nanocomposites revealed enhancement in viscosity with increasing ZnO loading. Maximum viscosity of 0.01Pa-s was obtained for 5wt% ZnO loading.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.