In this paper we present the recent progress in the growth of (1 0 0) HgCdTe epilayers using metal organic chemical vapour deposition on GaAs epi-ready substrates. Particular progress has been achieved in the reduction of macro-defects known as “hillocks”, revealed on the surface of HgCdTe epilayers with (1 0 0) crystallographic orientation. The large-scale defects can arise from such sources as poor substrate processing, dust and remnants from previous deposition, and non optimal parameters of nucleation and growth process. In our experiment, hillocks density was decreased to <102 cm−2 by proper choice of the growth parameters.Obtained epilayers are suitable for device fabrication. So far, significant improvements has been obtained in photoconductors operated at near-room temperatures. Devices fabricated from (1 0 0) HgCdTe have about one order of magnitude higher voltage responsivity than their (1 1 1) B counterparts.