Abstract
The cavitation erosion of ductile cast iron with ferrite–pearlite microstructure was analyzed based on ultrasonic experiments performed according to ASTM G32-2010 and the resistance was compared to the C45 steel with similar hardness. The microstructural observation of the surface for different exposure times to the ultrasonic cavitation reveals the fact that the process initiates at the nodular graphite–ferrite interface and is controlled by micro-galvanic activities and mechanical factors. The cavitation erosion resistance was evaluated based on the evolution of the mean depth erosion and the mean depth erosion rate as a function of the cavitation time. The cavitation erosion rate of the cast iron is up to 1.32 times higher than the one of the C 45 steel with similar hardness. This is explained by the occurrence of stress concentrators due to the expulsion of the graphite from the metallic matrix.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.