Abstract
Synthesis of ultralow density aerogels requires full transformation of diluted monomers into solid. Shrinkage during ageing and supercritical drying must be controlled as low as possible. Reported investigations deal with achievement in the optimisation of the two-step process parameters performed using classical acid and basic steps. Acid step involves the formation of partially hydrolysed and partially condensed silica mixture in ethanol. Different compositions of tetraethoxysilane, ethanol and hydrochloric acid (TEOS:ETOH:HCl) have been prepared to provide suitable gelling time and to enhance mechanical properties of final gels. Supercritical drying was performed using modified solutions mixtures which prevent silica dissolution. Under these conditions gel texture is preserved as demonstrated by the low shrinkage. This route permits positioning of uncracked transparent aerogels with densities lower than 3 kg/m 3. Specific surface area values are in the range of usual aerogels. Therefore, because of their unusual large pores, specific surface area decreases with density.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.