Abstract
Compositionally and structurally abrupt Si/SiO2 interfaces were prepared under ultrahigh vacuum conditions by RF plasma oxidation of Si(111) substrates with thermalized neutral oxygen atoms. The chemical, structural and electronic properties of the interface were analyzed and discussed with respect to a possible application in photovoltaic Si/SiO2 quantum well structures. The benefits of using neutral atomic oxygen were explored and turned out to be manifold: ultrathin SiO2 layers (thickness: 1–2 nm) can be precisely grown, the formation of suboxides is mostly suppressed and abrupt Si/SiO2 interfaces are obtained even at moderate substrate temperatures of 300 to 600 °C. Due to the perfect Si/SiO2 interfaces, the SiO2 layers allow thermal post-oxidation treatment up to 1000 °C without significant change in oxide thickness or stoichiometry. This is an essential prerequisite for the envisaged realization of Si/SiO2 superlattices with high crystallinity and low strain. It was shown that a post-oxidation annealing step lowers the strain and disorder at the interface resulting in lower intrinsic density of interface states. A further decrease of the density of interface states was achieved by hydrogen passivation as a result of saturation of dangling bonds.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.