Abstract
This work discusses the response of ultrafine-grained tungsten materials to high-flux, high-fluence, low energy pure He irradiation. Ultrafine-grained tungsten samples were exposed in the Pilot-PSI (Westerhout et al 2007 Phys. Scr. T128 18) linear plasma device at the Dutch Institute for Fundamental Energy Research (DIFFER) in Nieuwegein, the Netherlands. The He flux on the tungsten samples ranged from 1.0 × 1023–2.0 × 1024 ions m−2 s−1, the sample bias ranged from a negative (20–65) V, and the sample temperatures ranged from 600–1500 °C. SEM analysis of the exposed samples clearly shows that ultrafine-grained tungsten materials have a greater fluence threshold to the formation of fuzz by an order or magnitude or more, supporting the conjecture that grain boundaries play a major role in the mechanisms of radiation damage. Pre-fuzz damage analysis is addressed, as in the role of grain orientation on structure formation. Grains of (1 1 0) and (1 1 1) orientation showed only pore formation, while (0 0 1) oriented grains showed ripples (higher structures) decorated with pores. Blistering at the grain boundaries is also observed in this case. In situ TEM analysis during irradiation revealed facetted bubble formation at the grain boundaries likely responsible for blistering at this location. The results could have significant implications for future plasma-burning fusion devices given the He-induced damage could lead to macroscopic dust emission into the fusion plasma.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.