Abstract
An extensively investigated high-entropy alloy (HEA), Al0.1CoCrFeNi, is processed by dynamic equal channel angular pressing (D-ECAP) and subsequent annealing. Severe shear deformation and ultrahigh strain rate give rise to simultaneous activation of the {111}〈112〉 macro deformation twins and kink bands with the 〈110〉 or 〈112〉 rotation axes. Secondary kink bands are also observed in primary kink bands. With increasing annealing temperature, the deformation twins and kink bands both become less or disappear. The yield strength is increased by ∼255% solely by D-ECAP compared to the as-cast HEA. A reasonable combination of high strength and good ductility is achieved through annealing twins in recrystallized grains via annealing the D-ECAP-processed alloy at 900 °C. It is the first observation on kink bands within a face-centered cubic HEA under various loading conditions. The strengthening in these D-ECAP-processed samples before and after annealing is discussed in terms of grain boundary strengthening and dislocation strengthening.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.