Abstract
Rapid sintering of Li7La3Zr1.75Nb0.25Al0.15O12 (LLZO) is reported. The selection of heating elements, the effect of powder preparation and MgO additions in rapid sintered LLZO are described. Annealing LLZO powder at 750 ºC for 2 h in argon immediately before pressing helped to minimize porosity. A 15–20 s hold at 1372 ºC was sufficient to achieve densities >97%. The total sintering schedule time for rapid sintering represents a 99.7% decrease in sintering time compared to conventional sintering. At 70 °C under a pressure of 4.12 MPa cells had a critical current density of 1020 µA/cm2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.