Abstract
ABSTRACTUltra-low-temperature process treatments could raise tool steel wear resistance through microstructural change that occurs on the material, enhancing, that way, tools and dies lifetime. To investigate the tool steel wear resistance impact, micro-abrasive wear tests were carried out and an analysis based on the Archard’s law was considered, evaluating specimen mass loss by laser interferometry. Micro-hardness, X-ray diffractometry, scanning and optical microscopy and carbides quantitative evaluation were carried out aiming to material characterisation. Results demonstrated a micro-hardness improvement, ranging from 0.9–4.7% for the cryogenically treated specimens, when compared to the bulk material. This effect is related, mainly, to the retained austenite transformation and to the increase of fine secondary carbides dispersed amount in the martensitic matrixes cryogenically treated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.