Abstract
Herein, nominal compositions of MgAl2–x(Zn2/3Nb1/3)xO4 (x = 0.00, 0.04, 0.08, 0.12, 0.16, 0.20, 0.30, 0.40, and 0.50) ceramics are synthesized using a solid‐phase reaction method. The (Mg/Zn)Al2O4 solid solution and second‐phase Mg4Nb2O9 greatly improve the microwave dielectric properties of the samples. Moreover, the second phase, ionic polarizability, and relative density affect the dielectric constant (εr) value. The quality factor (Qf) value is correlated with the packing fraction, achieving a maximum value of ≈563 000 GHz at x = 0.40. The temperature coefficient of the resonant frequency (τf) value is negatively correlated with the B‐site bond value. When x = 0.40, the nominal composition MgAl1.6(Zn2/3Nb1/3)0.4O4 ceramic exhibits good microwave dielectric properties: εr = 9.06, ultrahigh Qf = 563 000 GHz, and τf = –45 ppm °C−1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.