Abstract
In this paper we present a method to deposit thin films of bismuth with sub-nanometer surface roughness for application to diamagnetic levitation. Evaporated films of bismuth have a high surface roughness with peak to peak values in excess of 100nm and average values on the order of 20nm. We expose the smooth backside of the films using a template stripping method, resulting in a great reduction of the average surface roughness, to 0.8nm. Atomic force microscope and X-ray diffraction measurements show that the films have a polycrystalline texture with preferential c-axis orientation. On the back side of the film, fine grains are grouped into larger clusters. Cantilever resonance shift measurements indicate that the Young's modulus of the films is on the order of 20GPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.