Abstract
Two-dimensional Fe-beidellite/carbon (Fe-BEI@C) superlattice-like heterostructure was prepared by intercalation of glucose in the gallery of layered Fe-BEI followed by calcination. The interlaminar and superficial carbon coating enables Fe-BEI to have good rate performance, fast lithium-ion diffusion, and high pseudocapacitance contribution, leading to excellent lithium storage performance as anode material for lithium-ion batteries (LIBs). The Fe-BEI@C/Li half cell delivers a maximum specific capacity of 850 mAh·g-1 at 0.5 A·g-1 and has a 92.3% retention rate after 100 cycles along with a high-rate performance of 403 mAh·g-1 at 5 A·g-1. The reversible valence state change of Si2+/Si4+ and Fe0/Fex+ (0 < x < 3) in electrochemical cycles are realized without collapse of layered structure. Additionally, the Fe-BEI@C heterostructure displays a high Li+ diffusion coefficient of 10-13∼10-10 cm2 s-1, illustrating fast Li+ transfer in the interlayer of Fe-BEI@C heterostructure. Dynamic analysis reveals that the Si redox reaction is almost dominated by surface control and that of Fe is mainly diffusion-controlled. This work has exploited a novel layered silicate as anode material for LIBs and developed a molecular-level carbon hybridization method to improve their electrochemical performance, which is meaningful for the application of layered silicate in the energy-storage field.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.