Abstract
Continuous strip casting and direct rolling method are receiving attention as the integrated producing process to obtain wrought magnesium alloys. In this research, AZ61 strip was cast from molten metal by twin-roll strip caster and rolled by “Structure-Control rolling process”. The effects of casting conditions and rolling parameters on surface aspects and microstructure of the rolled sheet were investigated. The results obtained were as follows: (1) By casting 1.5mm strip, a better surface and finer microstructure were obtained compared to 3mm strip. (2) By using structure-control rolling with R.T. pass, a microstructure of mean grain size of 5μm was obtained. (3) By lowering the starting rolling temperature, mean grain size and duplex grain size degree decreased and hardness increased. In addition, the deformation resistance decreased and the fracture strain increased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.