Twin boundary spacing effects on shock response and spall behaviors of hierarchically nanotwinned fcc metals

Abstract

Atomistic deformation mechanisms of hierarchically nano-twinned (NT) Ag under shock conditions have been investigated using a series of large-scale molecular dynamics simulations. For the same grain size d and the same spacing of primary twins λ1, the average flow stress behind the shock front in hierarchically NT Ag first increases with decreasing spacing of secondary twins λ2, achieving a maximum at a critical λ2, and then drops as λ2 decreases further. Above the critical λ2, the deformation mechanisms are dominated by three type strengthening mechanisms: (a) partial dislocations emitted from grain boundaries (GBs) travel across other boundaries; (b) partial dislocations emitted from twin boundaries (TBs) travel across other TBs; (c) formation of tertiary twins. Below the critical λ2, the deformation mechanism are dominated by two softening mechanisms: (a) detwinning of secondary twins; (b) formation of new grains by cross slip of partial dislocations. Moreover, the twin-free nanocrystalline (NC) Ag is found to have lower average flow stress behind the shock front than those of all hierarchically NT Ag samples except the one with the smallest λ2 of 0.71 nm. No apparent correlation between the spall strength and λ2 is observed in hierarchically NT Ag, since voids always nucleate at both GBs and boundaries of the primary twins. However, twin-free NC Ag is found to have higher spall strength than hierarchically NT Ag. Voids can only nucleate from GBs for twin-free NC Ag, therefore, twin-free NC Ag has less nucleation sources along the shock direction when compared to hierarchically NT Ag, which requiring higher tensile stress to create spallation. These findings should contribute to the understandings of deformation mechanisms of hierarchically NT fcc metals under extreme deformation conditions.