Abstract
In order to enhance the magnetoresistance (MR) of perpendicular magnetic tunnel junctions (pMTJs) based on MnGa alloys, a single ferromagnetic layer such as Fe and Co was previously inserted between MnGa and MgO barrier. In this study, to further enhance the spin-filter effect, we introduced a Fe/Co bilayer as an interlayer in the MnGa/MgO interface. Compared to the single Co interlayer, an apparent MR ratio enhancement was obtained when Fe layer thickness was around 0.3 nm for pMTJs with MnGa compositions of Mn57Ga43, Mn62Ga38, and Mn70Ga30, and the maximum MR ratio reaches 50% at room temperature. In addition, inverted magnetoresistance loops were observed due to the antiparallel alignment of the magnetic moments of Co and MnGa layers separated by the thin Fe layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.