Abstract
In order to modify the room-temperature plasticity of TiAl-based alloy, grain boundary character distribution (GBCD) in TiAl-based alloy was tuned through multidirectional isothermal forging (MDIF) combined with annealing. The experimental results showed that MDIF provided appropriate driving force for the regeneration of the coincidence site lattice (CSL) boundaries through recovery and recrystallization process. Combination of MDIF and annealing at 1100 °C for 90 min promoted the formation of a large number of annealing twins and increased the fraction of low-ΣCSL boundaries to 65.88% and the ratio of (Σ9+Σ27)/Σ3 to 15.12%, which contributed to the disruption of random boundary networks and enhanced the room-temperature plasticity of the TiAl-based alloy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.