Abstract
AbstractTo reveal the effect of ceria particle size on dispersion and structure of supported Pt catalysts during preparation, activation, and reaction testing, a unique CeO2/Al2O3 support (CA−c) with smaller CeO2 particle size and more surface defects was prepared using a colloidal CeO2 precursor, comparing with a conventional CeO2/Al2O3 support (CA−n) using cerium nitrate as precursor. More atomically dispersed Pt and abundant Pt−O−Ce structures were observed in the Pt/CA−c catalyst than in the Pt/CA−n catalyst. Both parent catalysts received significant enhancement on their catalytic CO oxidation activities if activated by 10% hydrogen at 400 °C before reaction. Between the two representative catalysts, the extent of activity enhancement upon activation was more pronounced for Pt/CA−c. We found that smaller Pt clusters with more active ionic Pt sites were generated on the activated Pt/CA−c catalyst, while agglomerated larger Pt particles with more metallic sites were formed on the activated Pt/CA−n. The facile formation of Ce3+ was also indicative of more active metal‐support interfaces in the activated Pt/CA−c catalyst. These results highlight the importance of regulating ceria support particles to enable a controlled anchoring and subsequent activation of Pt single atoms for low‐temperature CO oxidation reaction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.