Tuning of structural, light emission and wetting properties of nanostructured copper oxide–porous silicon matrix formed on electrochemically etched copper-coated silicon substrates

Abstract

Matrices of copper oxide–porous silicon nanostructures have been formed by electrochemical etching of copper-coated silicon surfaces in HF-based solution at different etching times (5–15 min). Micro-Raman, X-ray diffraction and X-ray photoelectron spectroscopy results show that the nature of copper oxide in the matrix changes from single-phase copper (I) oxide (Cu2O) to single-phase copper (II) oxide (CuO) on increasing the etching time. This is accompanied with important variation in the content of carbon, carbon hydrides, carbonyl compounds and silicon oxide in the matrix. The matrix formed at the low etching time (5 min) exhibits a single broad “blue” room-temperature photoluminescence (PL) band. On increasing the etching time, the intensity of this band decreases and a much stronger “red” PL band emerges in the PL spectra. The relative intensity of this band with respect to the “blue” band significantly increases on increasing the etching time. The “blue” and “red” PL bands are attributed to Cu2O and porous silicon of the matrix, respectively. In addition, the water contact angle measurements reveal that the hydrophobicity of the matrix surface can be tuned from hydrophobic to superhydrophobic state by controlling the etching time.