Abstract
ABSTRACTThis study reports on the structural and magnetic characterizations of free-standing bismuth ferrite, BiFeO3, nanoparticles synthesized in polyol medium. Fine tuning of the ferrite magnetic properties was achieved by adding an excess bismuth species or doping with cobalt ions, coupled with thermal annealing. Crystalline Bi1-yCoyFeO3 powders (where ‘y’ ranges from 0.00 to 0.10) were produced after annealing the precursors for one hour at 700οC. The average crystallite size was calculated to be approximately 22 nm. We found that the synthesis under stoichiometric excess of Bi species (up to 10 at.%) promoted a more complete crystallization of the material, i.e., no precursor phases remained. Furthermore, both the saturation magnetization and the coercivity of the synthesized powders were strongly influenced by the concentration of Co. They increased from 0.13 emu/g and 19 Oe to 3.5 emu/g and 1183 Oe for pure BiFeO3 and 10 at.% Co-doped BiFeO3, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.