Tuning of adhesion and disintegration of oxidized starch adhesives for the recycling of medium density fiberboard

Abstract

Oxidized starch (OS) adhesives with a balance between their adhesion and disintegration properties were prepared by controlling the degree of oxidation and modifying the cross-linker type and level to replace urea-formaldehyde (UF) resins for easy recycling of medium density fiberboard (MDF). Four molar ratios of H2O2/starch, two types of cross-linker, i.e., blocked-pMDI (B-pMDI) and citric acid (CA), and three levels of the cross-linkers were employed to tailor the performance of the OS adhesives. The OS reacted with the isocyanate groups from the B-pMDI to form amide linkages, while it formed ester linkages by reacting with the CA. The resulting B-pMDI/OS-bonded MDF had better physical and mechanical properties than the CA/OS-bonded MDF, with comparable adhesion (0.34 MPa) to UF resins and ten times greater degree of fiber disintegration than UF resins. The combination of a 0.5 molar ratio OS with 7.5 wt% of B-pMDI produced MDF exhibiting an optimal balance between adhesion and disintegration, suggesting that such OS adhesives could someday replace UF resins in manufacturing and recycling of MDF without formaldehyde emission.