The Ce3+, Mn2+-codoped calcium fluorapatite [Ca5(PO4)3F, FAP] nanorods were prepared by a simple hydrothermal method. SEM and TEM images indicate that the FAP : Ce3+, Mn2+ sample consists of nanorods with lengths around 30–70 nm and diameters around 20 nm, respectively. The as-obtained FAP nanorods show an intense bright blue emission (centered at 432 nm, lifetime 7.5 ns) arising from CO2˙− radical impurities in the crystal lattice under UV light irradiation. In addition, codoped with Ce3+ and Mn2+, the as-synthesized FAP : Ce3+, Mn2+ sample shows the tunable luminescence from blue to white to yellow by the variation of excitation UV light. The emission spectra of the as-synthesized FAP : Ce3+, Mn2+ sample show three broad bands, which are associated with the CO2˙− radical impurities (blue emission), Ce3+ ions (ultraviolet emission), and Mn2+ ions (yellow emission), respectively. The coexistence of three broad emissions results in the bright white light directly under suitable excitation wavelength. The combination emissions of impurities and metal activator ions may provide a novel strategy to obtain white light and tunable luminescence.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.