The Ti-Ni-Hf shape memory alloy powders were prepared by plasma rotating electrode process. And the powders were featured with the perfect sphericity and smooth surface. Moreover, the grain size was refined in the Ti-Ni-Hf alloy powders due to the rapid cooling rate during plasma rotating electrode process. It was found that the Ti-Ni-Hf alloy powders had the typical self-accommodation configuration including spear-like, mosaic-like and lath-like martensite. Various twins, such as (001) compound twin, (011) type I twin as well as {111} type I twin, were observed in Ti-Ni-Hf alloy powders. Differing from the bulk Ti-Ni-Hf alloy, two-stage transformation corresponding to B2⇌B19’ martensitic transformation was detected in the as-received Ti-Ni-Hf alloy powders. In addition, the martensitic transformation behaviors were closely related to the annealing temperatures. The Ti-Ni-Hf alloy powders with low annealing temperature of 500 °C still exhibited two-stage martensitic transformation, while two-stage martensitic transformation changed into single martensitic transformation in the Ti-Ni-Hf alloy powders with the higher annealing temperature of 900 °C. And finally the possible mechanisms for the evolution of martensitic transformation behaviors were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.