The tribological properties of a low-alloy steel surface treated by sulfur ion implantation (concentration range 1–30 at.%) have been tested under boundary lubrication conditions and compared with untreated steel. Pin-on-disc wear tests, carried out at constant load and speed, showed that sulfur implantation of the discs had a pronounced wear-reducing effect, leading to an up to three times longer sliding length before breakdown of the lubricating system (scuffing). Sulfur implantation (at high doses) amorphized the steel surface and led to the formation of nano-crystallites of the hexagonal FeS compound, which is supposed to have very beneficial lubricating properties. The transfer of a sulfur containing tribofilm to the pin counterface was observed at high sulfur doses and static load conditions. Under oscillating load conditions, the tribofilm transfer mechanism was apparently much less effective. The final state of the discs was characterized by very smooth, polished wear tracks, irrespective of implantation level. A significant fraction of the implanted sulfur remained in the wear tracks up to the critical friction coefficient.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.