Abstract
Tribological properties of diamond-like carbon (DLC) films in water were investigated concerning with the influence of surface roughness and various mating materials. The DLC films were deposited by pulsed-bias CVD method on AISI630 stainless steel. The substrate roughness ( R a) is in the range of 1.4–740 nm. AISI 440C, AISI 304 stainless steel and brass balls were used as a mating ball. The friction coefficients of DLC films against with AISI 440C stainless steel ball indicated under 0.1 irrespective of the roughness. The film having smooth surface ( R a=1.4 nm) had severe damage at a load of 9.4 N. However, the film having rough surface ( R a=263 nm) had no damage at the same load. The specific wear rate of the steel ball increased with increase of roughness of the surface. In the case of AISI 304 stainless steel ball, the specific wear rate of the ball showed similar tendency. The friction with brass ball showed relatively high friction coefficient in the range of 0.12–0.25. However, the damage on the films could not be observed after friction test. It is considered that the roughness of the surface is important factor for the rupture of the film in water environment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.