Abstract
PurposeDissimilar materials found applications in the structural fields to withstand the different types of loads and provide multi-facet properties to the final structure. Aluminum alloy materials are mostly used in aerospace and marine industries to provide better strength and safeguard the material from severe environmental conditions. The purpose of this study is to develop new material with superior strength to challenge the severe environmental conditions.Design/methodology/approachIn the present investigation, friction stir welding (FSW) dissimilar joints were prepared from AA6061 and AA5083 aluminum alloys, and the weld nugget (WN) was reinforced with hard reinforcement particles such as La2O3 and CeO2. The tribological and mechanical properties of the prepared materials were tested to analyze the suitability of material in the aerospace and marine environmental conditions.FindingsThe results showed that the AA6061–AA5083/La2O3 material exhibited better mechanical and tribological characteristics. The FSW dissimilar AA6061–AA5083/La2O3 material exhibited lower wear rate of 7.37 × 10−3 mm3/m and minimum friction coefficient of 0.31 compared to all other materials owing to the reinforcing effect of La2O3 particles and the fine grains formed by FSW process at WN region. Further, FSW dissimilar AA6061–AA5083/La2O3 material displayed a maximum tensile strength and hardness of 378 MPa and 118 HV, respectively, among all the other materials tested.Originality/valueThis work is original and novel in the field of materials science engineering focusing on tribological characteristics of friction stir welded dissimilar aluminum alloys by the reinforcing effect of hard particles such as La2O3 and CeO2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.